Stainless TIG wire for dissimilar steels

Home > Filler materials > Stainless TIG wire for dissimilar steels

Stainless TIG wire for dissimilar steels


Inox tig rod designed for welding dissimilar steels and those with 13% manganese content. Suitable for heterogeneous cold welding, without preheat, of carbon, stainless, wear-resistant and armor steels. It is also used as a cushion layer and cladding intermediary layers. Resistance to hot cracking is provided by the high manganese content. In some cases this rod may offer an alternative to high nickel weld metal in joints between cast iron and stainless steels. Used as a wear-resistant material of rails which work hardens from 200 to 400 HV.

(AWS A 5.9: ER307)
EN ISO 14343-A: W 18 8 Mn
Box 5 Kg 5
Box 25 Kg 25
14% Mn steels
13-17% Cr steels
C 0.07
Mn 7.00
Si 0.85
Cr 18.50
Ni 8.00
Mo 0.10
Cu 0.10
1.2 mm
1.6 mm
2.0 mm
2.4 mm
3.2 mm
4.0 mm
Yield strength 500 MPa
Tensile strength 660 MPa
Elongation 34 %
All positions
INOX MANGAN Semi-basic electrode for dissimilar steels
INEFIL INOX 307 SI Solid stainless steel wire for dissimilar steels