Double coated basic stick electrode for carbon and C - Mn steels

Special double-coated basic stick electrode E 7016 to be used for the welding of carbon and carbon-manganese steels with tensile strength up to 510 MPa. Suitable for AC DC current. To be reconditioned at 250÷300°C for an hour (if necessary).

Classifications

AWS A 5.1: E7016
EN ISO 2560-A: E 38 2 B

REQUEST LISTING

DOWNLOAD DOCUMENTS

Double coated special basic electrode suitable for the welding of carbon and Carbon –Manganese steels with tensile strength up to 510 MPa. Very good Charpy values down to -30°C. Given its high efficiency, it is ideally suited for maintenance works guaranteeing excellent welding results on poorly prepared materials. Excellent bead aesthetics, fragile slag, easily removable and very low sprays. Hygroscopic coating. If necessary, recondition at 250 ÷ 300 ° C for one hour.

C	0.07
Si	0.50
Mn	1.20

Yield strength	470 MPa
Tensile strength	540 MPa
Elongation	26 %
Impact test Kv (-20°C)	70 J
Impact test Kv (-30°C)	50 J

Diameter (mm)	Length	Ampere
2.5	350	60-110
3.2	350	90-140
4.0	350	130-190

tutte tranne vertical down

INE RB 86