Mig Mag wire for welding high strength steels.

Solid wire AWS A 5.28: ER100S-G EN ISO 16834-A: G 69 4 M21 Mn3Ni1CrMo for GMAW welding H.Y.S. steels with 770 MPa. Good mechanical properties has applications in fabrications of HSLA (high-strength low-alloy) To be used under the shield of Ar+O2.

Classifications

AWS A 5.28: ER100S-G
AWS A 5.28: ER110S-G
EN ISO 16834-A: G 69 4 M21 Mn3Ni1CrMo
EN ISO 16834-A: G 69 5 M13 Mn3Ni1CrMo

Approvals

Marchio CE
ABS
DB
TÜV

Finishes

Copper free
Copper coated

REQUEST LISTING

DOWNLOAD DOCUMENTS

Low-alloy copper-coated solid wire with Ni-Cr-Mo additions designed for welding high yield strength steels with minimum tensile strength higher than 770 MPa. Excellent impact strength at low temperatures (up to -50°C). Suitable for the metal working industry, offshore fabrication, chemical and petrochemical industry. It also has applications in fabrications of HSLA (high-strength low-alloy) steels, which may be used for industrial machinery construction, cranes and other highly stressed structural components. To be used under the shield of Ar+CO2 or Ar+O2.

C	0.08
Si	0.50
Mn	1.60
Cr	0.30
Mo	0.25
Ni	1.50
V	0.09

	M21	M13
Yield strength	750 MPa	790 MPa
Tensile strength	820 MPa	840 MPa
Elongation	19 %	20 %
Impact test Kv (-20°C)	90 J	100 J
Impact test Kv (-40°C)	60 J	80 J
Impact test Kv (-50°C)		60 J

Diameter (mm)	Volts	Ampere
0.8	16-28	60-200
1.0	17-32	80-260
1.2	18-34	100-360
1.6	19-38	130-450