Rutile-coated electrode with low carbon concentration designed for welding stainless steel with 19% Cr, 12% Ni and 2-3% Mo content with service temperature up to 400°C. It finds application in pipes fabrication, weld overlay, vessels & boilers fabrication, ship building and marine or salt environment. Generally good resistance to corrosion, intercrystalline corrosion and to many acids. Suitable for all positions, very good looking weld bead and easily removable slag.
C | 0.03 |
Mn | 1.00 |
Si | 0.70 |
Cr | 18.00 |
Ni | 12.00 |
Mo | 2.70 |
Yield strength | 440 MPa | |||
Tensile strength | 580 MPa | |||
Elongation | 35 % |
Diameter (mm) | Length | Ampere |
1.6 | 300 | 30-40 |
2.0 | 300 | 35-60 |
2.5 | 300 | 40-80 |
3.2 | 350 | 70-100 |
4.0 | 350 | 90-140 |