Rutile flux cored wire designed for welding Carbon and Carbon-Manganese steels with tensile strength up to 510 MPa. Main features: low spatter, fast freezing and easy to remove slag, excellent weld bead aspect. Small weld beads can be obtained in corner vertical up welding. Suitable for welding of steel building, road bridges and boilers, where good impact toughness is required at low temperature (down to -30°C). Specifically designed to be used in shipyards. To be used with CO2 shielding gas.
| C | 0.05 |
| Si | 0.45 |
| Mn | 1.30 |
| Shielding gas | C1 | |||
| Yield strength | 510 MPa | |||
| Tensile strength | 570 MPa | |||
| Elongation | 25 % | |||
| Impact test Kv (-20°C) | 70 J | |||
| Impact test Kv (-30°C) | 45 J |
| Diameter (mm) | Volts | Ampere |
| 1.0 | 15-28 | 90-240 |
| 1.2 | 16-34 | 110-340 |
| 1.4 | 17-35 | 130-360 |
| 1.6 | 19-36 | 140-440 |